采用浸渍法制备了用于催化湿式氧化工艺的负载型CuO／γ－Al2 O3催化剂，采用XRD、FT－IR、SEM对其进行了表征，并以CN－为目标污染物，考察了CuO／γ－Al2 O3催化剂的催化活性和稳定性。试验研究表明：催化剂中的活性组分Cu是以CuO的形式存在，并且成功负载于载体γ－Al2 O3；对于初始质量浓度为2000 mg ／L 的含氰废水，反应温度为130℃，搅拌速度为600 r／min，pH值为8，催化剂投加量为0．5 g／L，氧化剂30％ H2 O2用量为5 mL／L废水时，反应时间30 min，CN－去除率可达到99％以上；重复使用30次后，催化活性大幅度降低。%CuO/γ-Al2 O3 catalyst was prepared by impregnation method .X-ray diffraction(XRD),Fourier trans-form infrared spectroscopy (FT -IR) and scanning and electron microscope ( SEM) techniques were performed to characterize CuO/γ-Al2 O3 catalyst.The catalytic activity and stability of the prepared catalyst was investigated by cata-lytic wet oxidation process of cyanide-containing wastewater.The results show that active component Cu was detected in the form of CuO and was successfully loaded on the carrier γ-Al2 O3 .The 99 % CN- removal efficiency of 2 000 mg/L cyanide-containing wastewater could be attained in 30 min with the parameters of temperature of 130℃, stirring speed of 600 r/min,pH value of 8,reagent dosage of 0.5 g/L CuO/γ-Al2 O3 and oxidant 30%H2 O2 dosage of 5 mL/L.The catalytic activity was significantly decreased after being reused 30 times.
展开▼