Al/Pb/α-PbO2惰性阳极材料制备及电化学性能

关永永; 徐瑞东; 黄利平; 孔营; 陈步明

首页> 中文期刊> 《材料工程》 >Al/Pb/α-PbO2惰性阳极材料制备及电化学性能

Al/Pb/α-PbO2惰性阳极材料制备及电化学性能

开具论文收录证明 >>

期刊封面封底目录下载 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

采用单脉冲电沉积在铝合金基体表面制备了锌电积用Al/Pb/α-PbO2惰性阳极材料,研究了电沉积过程脉冲平均电流密度(2～5A ·dm-2)对制备的惰性阳极材料在50g·L-1Zn2+,150g ·L-1 H2SO4,35℃溶液中电化学性能的影响,测试了阳极极化、循环伏安和塔菲尔曲线.结果表明:增加脉冲平均电流密度,惰性阳极材料在[ZnSO4+H2SO4]溶液中同一测试电流密度下的析氧电位或析氧过电位逐渐升高.相比于Pb-1％ Ag合金阳极脉冲平均电流密度为2A ·dm-2时制备的惰性阳极材料在[ZnSO4+H2SO4]溶液中的析氧过电位较低,腐蚀电位较高,腐蚀电流较低.%Al/Pb/α-PbO2 inert anodes used in zinc electrowinning were prepared on the surface of aluminum alloy substrates by means of single-pulse electrodeposition, the influences of pulse average current densities from 2A·dm-2 to 5A·dm-2 on the electrochemical properties of the composite inert anodes in a synthetic zinc electrowinning electrolyte of 50g ·L-1 Zn2+ , 150g ·L-1 H2SO4 and 35℃ , were researched, and the anodic polarization, cyclic voltammetry and Tafel polarization curves were measured. The results show that in [ZnSO4 +H2SO4] electrolytes and at the same testing current density, oxygen evolution potential or overpotential of oxygen evolution of composite inert anodes gradually increase with the rise of pulse average current densities from an original plating bath. The inert anode prepared at 2A · dm-2 ,possessess lower oxygen evolution overpotential,higher corrosion potential and lower corrosion current than those of Pb-l%Ag alloy anode.

著录项

来源
《材料工程》 |2013年第2期|87-92|共6页
作者
关永永; 徐瑞东; 黄利平; 孔营; 陈步明;
展开▼
作者单位

昆明理工大学冶金与能源工程学院,昆明 650093;

云南省复杂有色金属资源清洁利用国家重点实验室(培育),昆明 650093;

昆明理工大学冶金与能源工程学院,昆明 650093;

云南省复杂有色金属资源清洁利用国家重点实验室(培育),昆明 650093;

中国科学院特种无机涂层重点实验室,上海 200050;

昆明理工大学冶金与能源工程学院,昆明 650093;

云南省复杂有色金属资源清洁利用国家重点实验室(培育),昆明 650093;

昆明理工大学冶金与能源工程学院,昆明 650093;

云南省复杂有色金属资源清洁利用国家重点实验室(培育),昆明 650093;

展开▼
原文格式 PDF
正文语种 chi
中图分类金属导电材料;
关键词
单脉冲; 电沉积; 电流密度; 惰性阳极材料; α-PbO2;