首页> 中文期刊> 《新型炭材料》 >CO-Mo/MgO催化剂上甲烷化学气相沉积制备高纯度多壁碳纳米管

CO-Mo/MgO催化剂上甲烷化学气相沉积制备高纯度多壁碳纳米管

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nearly uniform diameter multi-walled carbon nanotubes (MWCNTs) were synthesized over a magnesia sup-ported Co-Mo bimetallic catalyst through the catalytic chemical vapor deposition of methane. The bimetallic catalyst with a composition of Co: Mo: MgO =5: 20:75 ( mass ratio) was prepared by a sol-gel method. Thermagravimetric analysis shows that MWCNTs were synthesized in high yield. The selectivity of the catalyst for MWCNTs over undesired amor-phous carbon was 91.17%. Transmission electron microscopy indicates that the MWCNTs grown on the catalyst have an average diameter of 6.2±0.5 nm(mean±standard deviation). Through simple purification by mild acid treatment, the catalyst residue for the purified samples was reduced to 0.72%.%以甲烷为碳源,co-Mo/MgO为催化剂,通过气相化学沉积制备了直径均匀的多壁碳纳米管(MWC-NTs).采用溶胶-凝胶法所制双金属催化剂的组成为Co∶Mo∶MgO=5∶20∶75(质量比).热重分析表明多壁碳纳米管产率高达313.67%.催化剂对于多壁碳纳米管生长的选择性是91.17%(其余为无定形碳).透射电子显微镜分析显示:催化剂七生长的MWCNTs平均直径为6.2±0.5nm(平均±标准偏差).通过稀酸的简单纯化处理,纯化样品的催化剂残存率降至0.72%.

著录项

  • 来源
    《新型炭材料》 |2009年第2期|119-123|共5页
  • 作者

    Wei-Ming Yeoh; Kim-Yang Lee; Siang-Piao Chai; Keat-Teong Lee; Abdul Rahman Mohamed;

  • 作者单位

    School of Chemical Engineering, Engineering Campus, Universiti Sains Malaysia,Seri Ampangan, 14300 Nibong Tebal, S. P. S. Pulau Pinang, Malaysia;

    School of Chemical Engineering, Engineering Campus, Universiti Sains Malaysia,Seri Ampangan, 14300 Nibong Tebal, S. P. S. Pulau Pinang, Malaysia;

    School of Engineering, Monash University, Jalan Lagoon Selatan, 46150 Bandar Sunway, Selangor, Malaysia;

    School of Chemical Engineering, Engineering Campus, Universiti Sains Malaysia,Seri Ampangan, 14300 Nibong Tebal, S. P. S. Pulau Pinang, Malaysia;

    School of Chemical Engineering, Engineering Campus, Universiti Sains Malaysia,Seri Ampangan, 14300 Nibong Tebal, S. P. S. Pulau Pinang, Malaysia;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 特种结构材料;
  • 关键词

    催化; 多壁碳纳米管; 易脱除的催化剂; 催化化学气相沉积;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号