首页> 美国卫生研究院文献>Journal of Pharmaceutical Analysis >Electrochemical study and application on rutin at chitosan/graphene films modified glassy carbon electrode
【2h】

Electrochemical study and application on rutin at chitosan/graphene films modified glassy carbon electrode

机译：芦丁在壳聚糖/石墨烯薄膜修饰玻碳电极上的电化学研究及应用

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Graphene (G) was dispersed into 0.5% chitosan (Chit) solution, then the composite films were coated on glassy carbon electrode (GCE), the electrochemical behavior of rutin on a Chit/G modified GCE was investigated and the electrochemical parameters of rutin were calculated. Rutin effectively accumulated on the Chit/G/GCE and caused a pair of redox peaks at around 408 mV and 482 mV (vs. SCE) in 0.1 M phosphate buffer solution (pH 4.0). Under optimized conditions, the anodic peak current was linear to the rutin concentration in the range of 5×10−7–1.04×10−5 M. The regression equation was: y=9.9219x–0.0025, r= 0.9958. The proposed method was successfully used for the determination of rutin content in tablet samples with satisfactory results.
机译：将石墨烯（G）分散在0.5％的壳聚糖（Chit）溶液中，然后将复合膜涂覆在玻璃碳电极（GCE）上，研究芦丁在Chit / G修饰GCE上的电化学行为，并测定芦丁的电化学参数计算。芦丁有效积聚在Chit / G / GCE上，并在0.1M磷酸盐缓冲溶液（pH 4.0）中在408mV和482mV（vs.SCE）处产生一对氧化还原峰。在优化条件下，阳极峰值电流与芦丁浓度呈线性关系，范围为5×10 −7 –1.04×10 −5 M。回归方程为： y = 9.9219x–0.0025，r = 0.9958。该方法成功用于片剂中芦丁含量的测定，结果令人满意。