首页> 美国卫生研究院文献>Materials >Densification of Magnesium Aluminate Spinel Using Manganese and Cobalt Fluoride as Sintering Aids
【2h】

Densification of Magnesium Aluminate Spinel Using Manganese and Cobalt Fluoride as Sintering Aids

机译：以锰和氟化钴为烧结助剂的铝镁尖晶石致密化

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Highly dense magnesium aluminate spinel bodies are usually fabricated using pressure-assisted methods, such as spark plasma sintering (SPS), in the presence of lithium fluoride as a sintering aid. The present work investigates whether the addition of transition metal fluorides promotes the sintering of MgAl O bodies during SPS. At the same time, such fluorides can act as a source of optically active dopants. A commercial MgAl O was mixed with 0.5 wt% of LiF, MnF , and CoF and, afterwards, consolidated using SPS at 1400 °C. Although MnF and CoF promote the densification as effectively as LiF, they cause significant grain growth.
机译：在氟化锂作为烧结助剂的情况下，通常使用压力辅助方法（例如火花等离子体烧结（SPS））来制造高密度铝酸镁尖晶石体。目前的工作调查过渡金属氟化物的添加是否促进SPS期间MgAl O体的烧结。同时，此类氟化物可充当光学活性掺杂剂的来源。将市售的MgAl O与0.5 wt％的LiF，MnF和CoF混合，然后在1400°C下使用SPS固结。尽管MnF和CoF像LiF一样有效地促进了致密化，但它们引起了明显的晶粒长大。