首页> 美国卫生研究院文献>Polymers >Durability of Accoya Wood in Ground Stake Testing after 10 Years of Exposure in Greece
【2h】

Durability of Accoya Wood in Ground Stake Testing after 10 Years of Exposure in Greece

机译：希腊接触10年后亚福亚木材的耐久性

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this research, acetylated wood (Accoya) was tested in ground contact in central Greece. After ten years of exposure during a ground stake test, acetylated pine wood ( ) stakes, with a 20% acetyl weight gain, were completely intact and showed no visual decay (decay rating: 0). However, the key mechanical properties of Accoya wood, that is, modulus of elasticity (MOE) and modulus of rupture (MOR) after 10 years of ground contact, were significantly reduced by 32.8% and 29.6%, respectively, despite an excellent visual result since no evidence of fungal attack was identified. This contradiction could possibly indicate that the hallmarks of decay, i.e., brown-rot decay of acetylated wood can be the significant loss of mechanical properties before decay is actually visible.
机译：在本研究中，在希腊中部地区接触地接受测试乙酰化木材（亚孔岛）。经过十年的接触过程中的接地桩试验期间，乙酰化松木（）赌注，乙酰基重量增加20％，完全完全完整并显示出无视觉衰减（衰减等级：0）。然而，亚福亚木材的关键机械性能，即在10年后接地接触后的弹性模量（MOE）和破裂模量（MOE），分别显着降低了32.8％和29.6％，尽管存在很好的视觉结果由于没有确定真菌攻击的证据。这种矛盾可能表明腐烂的标志，即乙酰化木材的棕色腐烂衰减可以是腐烂在实际可见之前的机械性能的显着损失。