首页> 美国卫生研究院文献>Data in Brief >Evaluation of the corrosion resistance of a Ni-P coating deposited on additive manufacturing steel: A dataset
【2h】

Evaluation of the corrosion resistance of a Ni-P coating deposited on additive manufacturing steel: A dataset

机译：沉积在添加剂制造钢上Ni-P涂层的耐腐蚀性的评价：数据集

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This article presents the data set obtained for the research work entitled “Effect of a Ni-P coating on the corrosion resistance of an additive manufacturing carbon steel immersed in a 0.1 M NaCl solution” . Microstructural, mechanical, and electrochemical characterization (using the electrochemical impedance and electrochemical noise spectroscopy technique) is performed on a material obtained by additive manufacturing and the influence of a Ni-P coating on it. The layer sizes and hardness of the substrate are measured, as well as the thickness of the coating and its hardness, values for corrosion resistance, resistance to electrochemical noise and location indices are calculated. The data show an adequate deposition rate for the type of coating, as well as the increase in corrosion resistance when the coating is applied to the steel by additive manufacturing.
机译：本文介绍了为题为“Ni-P涂层对浸没在0.1M NaCl溶液中的添加剂制造碳钢的耐腐蚀性的影响”而获得的数据集。对通过添加剂制造获得的材料进行微观结构，机械和电化学谱表表征（使用电化学阻抗和电化学噪声光谱技术）对其进行Ni-P涂层的影响。测量基板的层尺寸和硬度，以及涂层的厚度及其硬度，计算耐腐蚀性的值，计算对电化学噪声的抗性和位置指数。数据显示涂层类型的足够沉积速率，以及通过添加剂制造将涂层施加到钢时耐腐蚀性的增加。