首页> 外文期刊>Advanced Functional Materials >Shape control of new Fe_xO-Fe_3O_4 and Fe_(1-y)Mn_yO-Fe_(3-z)Mn_zO_4 nanostructures
【24h】

Shape control of new Fe_xO-Fe_3O_4 and Fe_(1-y)Mn_yO-Fe_(3-z)Mn_zO_4 nanostructures

机译：新的Fe_xO-Fe_3O_4和Fe_（1-y）Mn_yO-Fe_（3-z）Mn_zO_4纳米结构的形状控制

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

New nanoparticle shapes of iron oxide (Fe_xO-Fe_3O_4, where 0.8 < x < 1) and iron-manganese oxide (Fe_(1-y)Mn_yO-Fe_(3-z)Mn_zO_4, where 0 < y < 1, and 0 < z < 3) were synthesized by decomposition of the corresponding metal formates in tri-n-octylamine/oleic acid mixtures at elevated temperatures (ca. 370 ℃), under an inert atmosphere. Details of the syntheses leading to the various shapes of nanoparticles are provided as a function of the reactions parameters, that is, precursor type and concentration, surfactant concentration, water concentration, reaction time, and temperature. Different electron microscopy techniques were used to characterize the crystal phases and the novel shapes of these nanostructures. Nanoparticles of Fe_xO-Fe_3O_4 were produced with different shapes, that is spheres, hexagons, and cubes, depending on the reaction conditions. By tuning the conditions, iron oxide nanocubes with concave faces were produced exclusively. Electron and X-ray diffraction data reveal these nanocubes to be single-crystal Fe_xO (wuestite) with small amounts of Fe_3O_4 (magnetite). For the mixed metal system, solid solutions of Fe_(1-y)Mn_yO with very small amounts of Fe_(3-z)Mn_zO_4 were observed, in which the produced oxide had a larger Fe:Mn ratio than present in the starting reagents. Adjusting the iron to manganese ratio in the mixed-metal nanoparticles resulted in different shapes. Nanoparticles with ca. 1:1 (Fe:Mn) ratios displayed a 'dog-bone-like' morphology, which can be considered a shape in between a pure Fe_xO-Fe_3O_4 nanocube and the rod-like nanostructures previously reported for the manganese oxide system. In general, higher Fe:Mn ratios (e.g., 9:1) in the product resulted in nanostructures with cubic shapes, while lower Fe:Mn values (e.g., 2:8) resulted in long (ca. 200 nm) rod-like nanostructures with flared ends. All of the nanostructures reported here exhibit internal structures that suggest a growth mechanism with etching on negatively curved rough crystal faces. Oxidation of the nanoparticles occurred with retention of their original shape.
机译：氧化铁（Fe_xO-Fe_3O_4，其中0.8

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号