摘要

Multifilamentary Nb/sub 3/Al superconducting wires for high field magnets above 20 T have been developed by a rapid-quenching process. A long length wire was produced, and a coil was fabricated using the wire. J/sub c/ of this wire was 195A/mm/sup 2/ at 20 T, 4.2 K and 486A/mm/sup 2/ at 20 T, 1.8 K, B/sub c2/ of the coil was 24.6 T at 4.2 K and 26.9 T at 1.8 K and the T/sub c/ was 17.8 K. In addition to investigating the stability, the residual resistance ratio was measured, the value was 16.9. Scattering of J/sub c/ in the longitudinal direction was examined and found to be within /spl plusmn/10%.
机译：通过快速淬火工艺开发了用于20 T以上高磁场磁体的多丝Nb / sub 3 / Al超导线。生产了长线，并使用该线制造了线圈。该线的J / sub c /在20 T，4.2 K时为195A / mm / sup 2 /在20 T，1.8 K时为486A / mm / sup 2 /在4.2 T时线圈的B / sub c2 /为24.6 T在1.8K下的K和26.9T以及T / sub c /为17.8K。除了研究稳定性之外，还测量了残余电阻比，该值为16.9。检查了J / sub c /在纵向上的散射，发现在/ spl plusmn / 10％以内。