首页> 外文期刊>Applied Surface Science >Hydrophobicity In Dlc Films Prepared By Electrodeposition Technique
【24h】

Hydrophobicity In Dlc Films Prepared By Electrodeposition Technique

机译：电沉积技术制备的Dlc膜的疏水性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Diamond-like carbon (DLC) films were deposited by electrodeposition technique onto SnO_2-coated glass substrates by using a mixture of acetic acid and water as electrolyte at a fixed applied voltage 2.14 V. The films showed two distinct broad Raman characteristic peaks located at ～1365 cm~(-1) (D-line) and 1575 cm~(-1) (C-line). Band gaps of the films varied between 1.98 and 2.35 eV. Hydrophobicity in these films was studied by measuring the contact angles of water droplets and it was found that the films were extremely hydrophobic. The results were interpreted in terms of hybridization of carbon in these DLC films.
机译：采用乙酸和水的混合液作为电解质，在固定电压为2.14 V的条件下，通过电沉积技术将类金刚石碳（DLC）膜沉积在镀SnO_2的玻璃基板上。该膜在〜处显示两个明显的宽拉曼峰。 1365 cm〜（-1）（D线）和1575 cm〜（-1）（C线）。薄膜的带隙在1.98和2.35 eV之间变化。通过测量水滴的接触角研究了这些膜中的疏水性，发现该膜是极疏水的。用这些DLC膜中碳的杂化来解释结果。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号