首页> 外文期刊>Applied Surface Science >Improved performance and stability by an Al/Ni bilayer cathode in organic light-emitting diodes
【24h】

Improved performance and stability by an Al/Ni bilayer cathode in organic light-emitting diodes

机译：Al / Ni双层阴极在有机发光二极管中的性能和稳定性得到改善

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Al/Ni bilayer cathode was used to improve the electroluminescent (EL) efficiency and stability in N,N'-bis(1-naphthyl)-N,N'-diphenyl-1,1' biphenyl 4,4'-dimaine (NPB)/tris-(8-hydroxyquinoline) aluminum (Alq(3))-based organic light-emitting diodes. The device with LiF/Al/Ni cathode achieved a maximum power efficiency of 2.8 lm/W at current density of 1.2 mA/cm(2), which is 1.4 times the efficiency of device with the state-of-the-art LiF/Al cathode. Importantly, the device stability was significantly enhanced due to the utilization of LiF/Al/Ni cathode. The lifetime at 30% decay in luminance for LiF/Al/Ni cathode was extrapolated to 400 It at an initial luminance of 100 cd/m(2), which is 10 times better than the LiF/Al cathode. (c) 2006 Elsevier B.V. All rights reserved.
机译：使用Al / Ni双层阴极来提高N，N'-双（1-萘基）-N，N'-二苯基-1,1'联苯4,4'-二胺（NPB）中的电致发光（EL）效率和稳定性）/三（8-羟基喹啉）铝（Alq（3））基有机发光二极管。具有LiF / Al / Ni阴极的器件在1.2 mA / cm（2）的电流密度下实现了2.8 lm / W的最大功率效率，是采用最新LiF /器件的效率的1.4倍。铝阴极。重要的是，由于使用了LiF / Al / Ni阴极，因此大大提高了器件的稳定性。将LiF / Al / Ni阴极在亮度衰减30％时的寿命推算为400 It，初始亮度为100 cd / m（2），这是LiF / Al阴极的10倍。 （c）2006 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号