Hydrogen-induced cracking of commercial purity titanium

C.F.Clarke; D.Hardie; B.M.Ikeda

首页> 外文期刊>Corrosion Science >Hydrogen-induced cracking of commercial purity titanium

【24h】

Hydrogen-induced cracking of commercial purity titanium

机译：氢致商业纯钛的裂解

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

Slow straining of compact tension specimens of commercial-purity titanium has been employed for assessing the likelihood of failure due to hydrogen pick-up in titanium containers for nuclear fuel waste disposal. Results indicate that slow crack growth occurs by a ductile tearing process at low hydrogen concentrations. No fast Crack growth occurs at such hydrogen levels, apparently because ductile collapse relaxes the stresses and prevents The attainment of a sufficiently high stress intensity for fast crack initiation.

机译：商用张力钛的紧凑张力试样的缓慢应变已用于评估由于钛容器中氢吸收引起的核燃料废物处置而导致失效的可能性。结果表明，在低氢浓度下，通过韧性撕裂过程会出现缓慢的裂纹扩展。在这样的氢含量下，不会出现快速的裂纹扩展，这显然是因为延性的塌陷松弛了应力并阻止了裂纹的产生。

著录项

来源
《Corrosion Science》 |1997年第9期|p.1545-1559|共15页
作者
C.F.Clarke; D.Hardie; B.M.Ikeda;
展开▼
作者单位

展开▼
收录信息美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
原文格式 PDF
正文语种 eng
中图分类金属腐蚀与保护、金属表面处理;
关键词
titanium; low strain-rate; hydrogen embrittlement;

机译：钛;低应变率氢脆;

相似文献

外文文献
中文文献
专利

1. An in-situ study on deformation and cracking initiation in oxygen-doped commercial purity titanium [J] . Shen Jianghua, Chen Biao, Umeda Junko, Mechanics of materials . 2020,第Sepa期

机译：氧气掺杂商业纯度钛变形和裂化起始的原位研究
2. Hydrogen-induced cracking in a very-high-purity high-strength steel [J] . X.-Y. Liu, J. Kameda, J.W. Anderegg, Materials Science and Engineering . 2008,第1a2期

机译：高纯度高强度钢的氢致裂纹
3. Hydrogen-Induced Cracking in GMA Welds of Vanadium-Titanium Microalloyed High Strength Steel [J] . K. Venkatesana* R. Sivasankarib V. Balusamyb Atul Saxenac Priti Jhac amp, Ramen Dattac Materials and Manufacturing Processes . 2010,第1a3期

机译：钒钛微合金高强度钢在GMA焊缝中的氢致裂纹
4. MICROSCOPIC FEATURES RELATED TO FATIGUE CRACK GROWTH IN COMMERCIAL-PURITY TITANIUM [C] . L. S. Rossino, C. A. R. P. Baptista, D. Rodrigues International Fatigue Congress . 2002

机译：商业纯度钛的疲劳裂纹生长相关的微观特征
5. FATIGUE CRACK INITIATION AND GROWTH OF MICROCRACKS IN COMMERCIAL PRECIPITATION HARDENED ALUMINUM - COPPER - MAGNESIUM ALLOYS OF ORDINARY AND HIGH PURITY [D] . KUNG, CHUNG YUAN. 1978

机译：普通高纯度铝铜镁合金硬质合金的商业沉淀疲劳裂纹的萌生和裂纹的扩展。
6. Mechanical Strength and Biocompatibility of Ultrafine-Grained Commercial Purity Titanium [O] . Yuri Estrin, Hyoun-Ee Kim, Rimma Lapovok, 2006

机译：超细颗粒商业纯钛的机械强度和生物相容性
7. Acoustic Emission Monitoring of Wet H2S Cracking of Linepipe Steels: Application to Hydrogen-Induced Cracking and Stress-Oriented Hydrogen-Induced Cracking [O] . V. Smanio, J. Kittel, M. Fregonese, 2011

机译：线皮钢湿H2S开裂的声发射监测：施用氢致裂纹和应力取向氢诱导的裂化
8. A FILM-RUPTURE MODEL OF HYDROGEN-INDUCED, SLOW CRACK GROWTH IN ALPHA-BETA TITANIUM [R] . Howard G. Nelson 1975

机译：aLpHa-BETa钛中氢致慢裂纹生长的薄膜破裂模型

Hydrogen-induced cracking of commercial purity titanium

摘要

著录项

相似文献

相关主题

期刊订阅