首页> 外文期刊>Materials Research Letters >Manipulating the powder size to achieve enhanced strength and ductility in harmonic structured Al alloy
【24h】

Manipulating the powder size to achieve enhanced strength and ductility in harmonic structured Al alloy

机译：控制粉末尺寸以提高谐波结构铝合金的强度和延展性

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The present work reports a simple one-step powder metallurgy approach for producing bulk fine-grained Al2024 alloy with a unique harmonic structure and superior mechanical properties. The grain size of the bulk specimen could be easily manipulated by changing the initial powder size. Tensile test suggested that the yield strength of the fine-grained specimen with an average grain size of 3.78?μm (powder size ～20?μm) was about 265?MPa, which was three times higher than that of the conventional coarse-grained counterpart, maintaining a good ductility (total elongation ～15%). The reasons for the unique microstructure and the enhanced mechanical properties were discussed.
机译：本工作报告了一种简单的一步法粉末冶金方法，用于生产具有独特的谐波结构和优异的机械性能的块状细晶粒Al2024合金。通过改变初始粉末尺寸可以很容易地控制大块试样的晶粒尺寸。拉伸试验表明，平均粒径为3.78？μm（粉体尺寸〜20？μm）的细粒试样的屈服强度约为265？MPa，是传统粗粒试样的三倍。 ，保持良好的延展性（总伸长率〜15％）。讨论了独特的微观结构和增强的机械性能的原因。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号