首页> 外文期刊>Revista Latinoamericana de Metalurgia y Materiales >ESTUDIO DE LA REMOCION DE IMPUREZAS DE ARCILLAS CAOLINíTICAS DEL ESTADO DE HIDALGO (MéXICO) ( STUDY OF REMOVING IMPURITIES OF KAOLIN CLAYS FROM HIDALGO STATE, (MEXICO) )
【24h】

ESTUDIO DE LA REMOCION DE IMPUREZAS DE ARCILLAS CAOLINíTICAS DEL ESTADO DE HIDALGO (MéXICO) ( STUDY OF REMOVING IMPURITIES OF KAOLIN CLAYS FROM HIDALGO STATE, (MEXICO) )

机译：喜达拉州（墨西哥）从高加索州（墨西哥）去除高岭土杂质的研究

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

En este trabajo se reporta el estudio de la remoción de impurezas y caracterización de arcillas de caolín procedentes de diferentes minas del Municipio de Agua Blanca de Iturbide, Hidalgo (México), tratadas con la finalidad de incrementar su índice de blancura las cuales fueron recolectadas mediante muestreo selectivo, procesadas por un método sencillo (tamizado, dispersión y asentamiento) y caracterizadas por difracción de rayos X (DRX), microscopía electrónica de barrido (MEB), análisis de tama?o de partícula (ATP), análisis químico con plasma acoplado (ICP) e índice de blancura (IB). Su procesamiento consistió en la trituración del mineral, atrición y cribado. Los productos finos de este último proceso (tama?os de partícula inferiores a 37 μm), fueron mezclados con agua desionizada a 45 por ciento de sólidos en peso adicionando 2 Kg Ton -1 de desfloculante y posteriormente diluidas a 20 por ciento de sólidos en peso, con el propósito de obtener partículas micrométricas. Los resultados pusieron en evidencia que el proceso de cribado separó el 30 % de arenas cuyos contenidos de sílice fueron superiores comparados con los contenidos en el material fino. Aplicando el proceso de asentamiento se obtuvieron partículas en suspensión con un tama?o promedio de 1,83 μm. Al realizar el estudio cristalográfico, además de la caolinita, se identificaron diferentes impurezas tales como sulfuros, óxidos y carbonatos. Mediante los estudios cristalográficos, análisis químicos por ICP y la medición del índice de blancura, se llevó a cabo el seguimiento de la disminución de impurezas en cada proceso de separación. Se obtuvo un concentrado final con tama?o promedio de partícula de 1,83 μm, un índice de blancura de 91,27% y una recuperación en peso global de 63 %. This paper reports the study of the removal of impurities and characterization of kaolin clays from different mines in Agua Blanca de Iturbide, Hidalgo (Mexico), treated with the aim of increasing its whiteness index which were collected by selective sampling, processed by a simple method (sieving, dispersal and settlement) and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), particle size analysis (ATP), chemical analysis coupled plasma (ICP ) and whiteness index (IB). The mineral was processed by crushing, attrition and screening. Sieving of fine products were mixed vigorously with deionized water at 45 percent solids in wt.% adding 1 Kg Ton -1 of dispersant. Subsequently, the pulp was diluted and settling at 20 percent solids, with the purpose of obtaining micron particles and finally a second settling was applied. The results showed that the sieving process removed 30% of silica sand whose contents were higher compared with those contained in the fine material. Applying the process of settling suspended particles were obtained with an average size of 1,83 μm. In the crystallographic study, in addition to kaolinite, were identified different impurities such as sulfides, oxides and carbonates. By crystallographic studies, chemical analysis by ICP and the whiteness index measurement was carried out monitoring of the reduction of impurities in each separation process. Final concentrate was obtained with average particle size of 1,83 μm, a whiteness index of 91,27% and an overall weight recovery of 63%.
机译：在这项工作中，从墨西哥伊达尔戈市的Agua Blanca de Iturbide市（墨西哥）的不同矿山进行了杂质去除和高岭土粘土表征的研究，以提高其白度指数，这些方法通过以下方法收集选择性采样，通过简单的方法（筛分，散射和沉降）进行处理，并通过X射线衍射（XRD），扫描电子显微镜（SEM），粒度分析（ATP），耦合等离子体化学分析进行表征（ICP）和白度指数（IB）。其处理包括矿物质的粉碎，磨损和筛选。将最后一步的精细产品（粒径小于37 µm）与去离子水混合，使其固体含量为45％（重量），加入2 Kg Ton -1的絮凝剂，然后稀释至20％的固体重量，以获得微米级颗粒。结果表明，筛选过程中分离出的二氧化硅含量比细料中更高的30％的沙子。通过进行沉降处理，得到平均粒径为1.83μm的悬浮粒子。进行晶体学研究时，除了高岭石外，还发现了不同的杂质，例如硫化物，氧化物和碳酸盐。通过晶体学研究，ICP化学分析和白度指数的测量，在每个分离过程中均监测了杂质的减少。得到最终浓缩物，其平均粒径为1.83μm，白度指数为91.27％，总重量回收率为63％。本文报道了在墨西哥伊达尔戈的Agua Blanca de Iturbide的不同矿山中去除杂质和表征高岭土的研究，目的是提高白度指数，该方法是通过选择性采样收集的，并通过一种简单方法进行处理（筛分，分散和沉降），并通过X射线衍射（XRD），扫描电子显微镜（SEM），粒度分析（ATP），化学分析耦合等离子体（ICP）和白度指数（IB）进行表征。通过粉碎，磨耗和筛选处理矿物。细筛与去离子水剧烈混合，固体含量为45％（重量），加入1千克吨-1的分散剂。随后，将纸浆稀释并以20％的固体沉降，以获取微米级颗粒，最后进行第二次沉降。结果表明，筛分过程除去了比细料中所含硅砂含量高的30％的硅砂。应用沉降过程得到的悬浮颗粒的平均尺寸为1.83 µm。在晶体学研究中，除高岭石外，还鉴定出不同的杂质，例如硫化物，氧化物和碳酸盐。通过晶体学研究，通过ICP进行化学分析和白度指数测量，以监测每个分离过程中杂质的减少。最终浓缩物的平均粒径为1.83 µm，白度指数为91.27％，总重量回收率为63％。