首页> 外文期刊>Revista Latinoamericana de Metalurgia y Materiales >ESTUDIO DE LA OBTENCIóN DE POLVOS DE UNA ALEACIóN Ag – ZnO MEDIANTE ALEADO MECáNICO Y MOLIENDA REACTIVA, PARA USO EN CONTACTORES ELéCTRICOS ( STUDY OF POWDERS PRODUCTION OF Ag-ZnO ALLOY BY MEANS OF MECHANICAL ALLOYING AND REACTION MILLING, FOR USE IN ELECTRICAL CONTACTS )
【24h】

ESTUDIO DE LA OBTENCIóN DE POLVOS DE UNA ALEACIóN Ag – ZnO MEDIANTE ALEADO MECáNICO Y MOLIENDA REACTIVA, PARA USO EN CONTACTORES ELéCTRICOS ( STUDY OF POWDERS PRODUCTION OF Ag-ZnO ALLOY BY MEANS OF MECHANICAL ALLOYING AND REACTION MILLING, FOR USE IN ELECTRICAL CONTACTS )

机译：机械合金化和反应铣削法生产Ag-ZnO合金的粉末的研究

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Este trabajo tuvo como objetivo estudiar la obtención de polvos de una aleación Ag-ZnO, mediante un proceso combinado de aleado mecánico y molienda reactiva. El procedimiento experimental se dividió en dos etapas. En la primera de ellas, granallas de Ag y Zn fueron aleadas mecánicamente bajo atmósfera de Ar, utilizando un molino SPEX 8000D. En la segunda etapa, los polvos obtenidos mediante aleado mecánico fueron sometidos a molienda reactiva, bajo atmósfera de aire y utilizando etanol como agente de control. La caracterización microestructural de los polvos fue realizada mediante difracción de rayos X y microscopía óptica. En base a los resultados obtenidos, se concluye que mediante la combinación de aleado mecánico y molienda reactiva, es posible obtener polvos con una fina y homogénea distribución de precipitados de ZnO en una matriz de Ag. The objective of this work was to study the production of powders of Ag-ZnO alloy by means of mechanical alloying and reaction milling. The experimental procedure was divided in two stages. During the first stage, Ag and Zn turnings were mechanically alloyed under Ar atmosphere using a SPEX 8000D mill. In the second stage, the powders obtained by mechanical alloying were milled under air using ethanol as process control agent. The powders microstructural characterization was carried out by X-ray diffraction and optical microscopy. Based on the results obtained it can be conclude that by means of combination of mechanical alloying and reaction milling processes it is possible to obtain a Ag-ZnO alloy with a fine and homogeneous distribution of ZnO precipitates.
机译：这项工作的目的是研究通过机械合金化和反应研磨相结合的方法从Ag-ZnO合金中获得粉末。实验过程分为两个阶段。在第一个中，使用SPEX 8000D轧机在Ar气氛下将Ag和Zn磨粒机械合金化。在第二阶段中，通过机械合金化获得的粉末在空气气氛下并使用乙醇作为控制剂进行反应性研磨。通过X射线衍射和光学显微镜对粉末进行微观结构表征。根据获得的结果，可以得出结论，通过机械合金化和反应性研磨的结合，可以得到在Ag基体中具有均匀分布的ZnO沉淀物的粉末，其目的是研究生产过程。机械合金化和反应铣削制备Ag-ZnO合金粉末。实验过程分为两个阶段。在第一阶段，使用SPEX 8000D轧机在Ar气氛下对Ag和Zn车削进行机械合金化。在第二阶段中，通过机械合金化获得的粉末在空气中使用乙醇作为工艺控制剂进行研磨。通过X射线衍射和光学显微镜对粉末进行微结构表征。基于获得的结果，可以得出结论，通过机械合金化和反应研磨工艺的组合，可以获得具有精细且均匀分布的ZnO沉淀物的Ag-ZnO合金。