The cooperative effects between the PANI (polyaniline)ano-NiO (nano nickel oxide) composite electrode material and redox electrolytes (potassium iodide, KI) for supercapacitor applications was firstly discussed in this article, providing a novel method to prepare nano-NiO by using β-cyelodextrin (β-CD) as the template agent. The experimental results revealed that the composite electrode processed a high specific capacitance (2122.75 F·g ?1 at 0.1 A·g ?1 in 0.05 M KI electrolyte solution), superior energy density (64.05 Wh·kg ?1 at 0.2 A·g ?1 in the two-electrode system) and excellent cycle performance (86% capacitance retention after 1000 cycles at 1.5 A·g ?1 ). All those ultra-high electrical performances owe to the KI active material in the electrolyte and the PANI coated nano-NiO structure.
机译：本文首先讨论了PANI（聚苯胺）/纳米NiO（纳米氧化镍）复合电极材料与用于超级电容器的氧化还原电解质（碘化钾，KI）之间的协同作用，提供了一种新的方法来制备纳米NiO。以β-环糊精（β-CD）为模板剂。实验结果表明，该复合电极具有较高的比电容（在0.05 M KI电解液中，在0.1 A·g？1时为2122.75 F·g？1），能量密度更高（在0.2 A·g下为64.05 Wh·kg？1）。在两电极系统中为？1）和出色的循环性能（在1.5 A·g？1的条件下进行1000次循环后，电容保持率为86％）。所有这些超高电性能归因于电解质中的KI活性材料和PANI涂层的纳米NiO结构。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号