首页> 外文期刊>Journal of Advanced Science >ホットプレス法によるMgB2バルクの作製と組織評価
【24h】

ホットプレス法によるMgB2バルクの作製と組織評価

机译：热压法制备MgB2块体及其微观结构评价

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

MgB_(2) bulks have been prepared by hot pressing method in order to fabricate high density MgB_(2) structure. Mixed Mg and B powder were enclosed in stainless steel mold. The bulk samples were treated at 850°C for 3 h under 30-300 MPa in Ar gas atmosphere. The hot pressed sample size is 20 mm in diameter and 5.6~10 mm in thickness. The XRD patterns of the bulks show that MgB_(2) phase is synthesized and dominant with small amount of MgO in the whole range of 0~300 MPa. The density of the bulks increased with increasing hot pressing pressure, and reached a peak of 2.34 g/cm~(3) at 200 MPa which corresponded to the relative density of 90 %.
机译：为了制造高密度的MgB_（2）结构，已经通过热压法制备了MgB_（2）块。将混合的Mg和B粉末封入不锈钢模具中。将大块样品在Ar气氛中在850°C和30-300 MPa下处理3小时。热压样品的直径为20毫米，厚度为5.6〜10毫米。块体的X射线衍射图谱表明，在0〜300 MPa的整个范围内，MgB_（2）相被合成并占主导地位，少量的MgO存在。堆密度随热压压力的增加而增加，在200 MPa时达到2.34 g / cm〜（3）的峰值，相当于90％的相对密度。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号