首页> 外文期刊>RSC Advances >Roll-to-roll slot die production of 300 mm large area silver nanowire mesh films for flexible transparent electrodes
【24h】

Roll-to-roll slot die production of 300 mm large area silver nanowire mesh films for flexible transparent electrodes

机译：卷对缝狭缝模具生产用于柔性透明电极的300毫米大面积银纳米线网状薄膜

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

To develop flexible transparent electrodes, an ink fabricated with silver nanowires (AgNWs) was coated on a polyethylene terephthalate substrate using a roll-to-roll slot die machine. The AgNW used in the manufacturing of the transparent electrode is a highly transparent conductive material that is very close to commercialization due to its low sheet resistance, low heat treatment temperature, and high transmittance. An AgNW ink was optimized for the slot die process, which was prepared using the optimized formulation with AgNWs, solvent, and dispersant. As a result, high-quality transparent conductive films were successfully manufactured with 32–94 Ω sq?1 of sheet resistance, 1.3–3.2 of haze and 86.2–92% transmittance with a width of 300 mm. To verify the possibilities in optoelectronic applications, organic solar cells were fabricated with the AgNW mesh transparent electrode and showed a good performance of 7.65% efficiency, which was better than the result obtained using an indium tin oxide-based electrode.
机译：为了开发柔性透明电极，使用卷对卷狭缝模切机将用银纳米线（AgNWs）制造的油墨涂覆在聚对苯二甲酸乙二醇酯基板上。在透明电极的制造中使用的AgNW是高度透明的导电材料，由于其低薄层电阻，低热处理温度和高透射率而非常接近商业化。针对狭缝模头工艺对AgNW油墨进行了优化，该油墨是使用具有AgNW，溶剂和分散剂的优化配方来制备的。结果，成功制造了具有32-94Ωsq ？1 薄层电阻，1.3-3.2雾度和86.2-92％透光率的高质量透明导电膜宽度为300毫米。为了验证在光电应用中的可能性，用AgNW网状透明电极制造了有机太阳能电池，并显示出7.65％的效率，这比使用铟锡氧化物基电极获得的结果更好。