首页> 外文期刊>RSC Advances >Centimeter-scale 2D perovskite (PEA)2PbBr4 single crystal plates grown by a seeded solution method for photodetectors
【24h】

Centimeter-scale 2D perovskite (PEA)2PbBr4 single crystal plates grown by a seeded solution method for photodetectors

机译：通过种子溶液法生长用于光电探测器的厘米级2D钙钛矿（PEA）2PbBr4单晶板

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Large-sized single-crystal two-dimensional (2D) perovskites are highly desirable owing to their fundamental properties and intriguing ability to boost devices. Herein, 2-phenylethylammonium lead bromide [(PEA) _(2) PbBr _(4) ] single crystals, which are a violet-light-emitting 2D perovskite material, with typical lateral sizes of about one centimeter were successfully grown using a seeded solution method. The single-crystal plates showed a well-defined shape (rectangle or hexagon), a natural thickness (300–500 μm) similar to that of conventional silicon and InP wafers, a large aspect ratio of ～20, and a smooth surface (root mean square, ～0.7 nm). We integrated these single crystal plates into an ultraviolet photodetector, achieving a low dark current of ～10 ~(?13) A and an efficient photoresponse (on/off ratio, ～10 ~(3) ). This experiment could easily be extended to grow freestanding 2D perovskite single crystals on a wafer scale for practical integrated optoelectronics.
机译：大型单晶二维（2D）钙钛矿由于其基本特性和增强器件的吸引力而非常受人们欢迎。在此，使用籽晶成功地生长了2-苯基乙基铵溴化铅[（PEA）_（2）PbBr _（4）]，这是一种发出紫光的二维钙钛矿材料，典型的横向尺寸约为一厘米。解决方法。单晶板具有清晰的形状（矩形或六边形），与常规硅和InP晶片相似的自然厚度（300-500μm），宽高比约为20，表面光滑（根均方根，约0.7 nm）。我们将这些单晶板集成到紫外光电探测器中，实现了约10〜（？13）A的低暗电流和有效的光响应（开/关比为〜10〜（3））。可以轻松地扩展该实验，以在晶圆级上生产独立的2D钙钛矿单晶，以用于实用的集成光电。