Nickel-nanoparticle-containing polyimide composite films were prepared by liquid-phase reduction of Ni ~(2+) ions with potassium borohydride (KBH _(4) ). The nanoparticles were amorphous with diameters of approximately 10–20 nm, depending on the KBH _(4) concentration and reduction temperature. At high KBH _(4) concentrations, the nanoparticles appeared to contain various nickel boride species. The number of nanoparticles and Ni content both increased upon repeated adsorption/reduction of Ni ~(2+) ions, where the particle growth was inhibited by the rigid polymer chain and the formation of smaller particles was favored.
机译：通过用硼氢化钾（KBH _（4））液相还原Ni〜（2+）离子制备含镍-纳米颗粒的聚酰亚胺复合膜。纳米粒子是无定形的，直径大约为10–20 nm，这取决于KBH_（4）的浓度和还原温度。在高KBH_（4）浓度下，纳米颗粒似乎包含各种硼化镍物质。重复吸附/还原Ni〜（2+）离子后，纳米颗粒的数量和Ni含量均增加，其中刚性聚合物链抑制了颗粒的生长，有利于形成较小的颗粒。