首页> 外文期刊>RSC Advances >Low temperature synthesis and characterization of single phase multi-component fluorite oxide nanoparticle sols
【24h】

Low temperature synthesis and characterization of single phase multi-component fluorite oxide nanoparticle sols

机译：低温合成与单相多组分氟铝氧化物纳米粒子溶胶的表征

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We report for the first time a simple, scalable approach for the synthesis of single-phase multi-component fluorite oxide nanoparticle sols: Gd _(0.2) La _(0.2) Y _(0.2) Hf _(0.2) Zr _(0.2) O _(2) (GLYHZ) and Gd _(0.2) La _(0.2) Ce _(0.2) Hf _(0.2) Zr _(0.2) O _(2) (GLCHZ) using chemical co-precipitation followed by peptization in acidic medium under mild conditions (≤80 °C). High resolution transmission electron microscopy (HRTEM) along with selected area electron diffraction (SAED) studies confirm fully crystalline single-phase cubic fluorite nanoparticles having a particle size of about 2–3 nm with a narrow size distribution was obtained. The powder X-ray diffraction (XRD) and Rietveld refinement studies of samples calcined at 500 °C for 4 hours confirm a single phase solid solution and a lack of secondary phases.
机译：我们首次报告一种简单，可扩展的单相多组分氟镁氧化物纳米颗粒溶胶的方法：Gd _（0.2）La _（0.2）y _（0.2）Hf _（0.2）Zr _（0.2 ）O _（2）（甘露出）和Gd _（0.2）La _（0.2）CE _（0.2）HF _（0.2）Zr _（0.2）o _（2）（GlCHz）使用化学共沉淀然后在温和条件下酸性培养基（≤80°C）染色。高分辨率透射电子显微镜（HRTEM）以及选定的区域电子衍射（SAED）研究确认了具有窄尺寸分布的粒径为约2-3nm的完全结晶单相立方萤石纳米颗粒。粉末X射线衍射（XRD）和RIETVELD细化研究在500℃下煅烧4小时的样品确认单相固溶溶液和缺少二次相。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号