首页> 外文期刊>RSC Advances >Ethylene brassylate-co-δ-hexalactone biobased polymers for application in the medical field: synthesis, characterization and cell culture studies
【24h】

Ethylene brassylate-co-δ-hexalactone biobased polymers for application in the medical field: synthesis, characterization and cell culture studies

机译：乙烯碳酸亚胺-Co-δ-六甲基球酮用于医疗领域的生物化聚合物：合成，表征和细胞培养研究

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Copolymers based on ethylene brassylate (EB) and δ-hexalactone (δ-HL), two monomers obtained from renewable sources, were synthesized with triphenyl bismuth by ring-opening polymerization. The poly(EB- co -δ-HL), with EB molar contents ranging from 49 to 90%, presented a slight deviation from the random distribution of sequences ( R > 0.71) while WAXS measurements proved that only the EB blocks were able to crystallize (with crystallinity degrees of ～23–39%). The low T _(g) s (
机译：基于乙基碳酸亚甲酯（EB）和δ-六甲烷酮（δ-HL）的共聚物，通过开环聚合用三苯基铋合成两种单体。具有49〜90％的EB-Co-Δ-H1），从49〜90％的范围内呈现出与序列的随机分布（R> 0.71）的略微偏差，而蜡测量证明只有EB块才能结晶（结晶度〜23-39％）。低T _（g）S（<α27℃），其结晶能力和熔化温度从50至65°C的熔化温度使得这些热塑性弹性体（良好的热稳定性）非常易于加工。同样，与聚（ε-己内酯）或聚（ω-五甲烷酮）（在21°C和37之间具有高伸长率之间的弹性模量）相比，它们的热性能导致了具有改善的灵活性，其具有改善的灵活性°C。另一方面，除了增加非晶特性之外，δ-H1掺入，带来了更无序的链微观结构分布，导致每天0.0028-0.0041的降解率较高。最后，使用人的皮肤成纤维细胞（HDFS）的代谢活性和细胞形态学研究表明，这些材料不是细胞毒性并为细胞提供有效的基材以连接和增殖，这意味着它们适用于生物医学领域。