首页> 外文期刊>ISIJ international >Effects of boron Addition on Tempering Processes in an Fe-9Cr-0.1C Alloy Martensite
【24h】

Effects of boron Addition on Tempering Processes in an Fe-9Cr-0.1C Alloy Martensite

机译：硼对Fe-9Cr-0.1C合金马氏体回火过程的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effects of boron addition on the tempering processes of 0.1C-9Cr martensite have been studied. The alloys with and without 98ppm boron were prepared. The specimens austenitized at 1200deg. C for 1.2 Ks were quenched into iced brine. The structure was consisted of a' martensite laths. They were heated at 10 deg. C/min to 900 deg. C. temperature derivative of electric resistivity, dp/dT, exhibited small increase at temperature around 740 deg. C (reaction A), gradual decrease at temperatures between 750 deg.C and 800 deg. C (reaction B), large decrease at around 815 deg. C (reaction C) and small increase at around 830 deg. C (reaction D).
机译：研究了硼对0.1C-9Cr马氏体回火过程的影响。制备具有和不具有98ppm硼的合金。标本在1200度奥氏体化。将1.2Ks的C淬灭到冰盐水中。结构由马氏体板条组成。将它们加热到10℃。 C / min至900摄氏度电阻率的温度导数dp / dT在740度左右的温度下显示出很小的增加。 C（反应A），温度在750摄氏度至800摄氏度之间逐渐降低。 C（反应B），在815度左右大幅降低。 C（反应C），并在830度左右小幅增加。 C（反应D）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号