首页> 外文期刊>ISIJ international >Thermodynamic Behavior of Carbon in Molten Slags
【24h】

Thermodynamic Behavior of Carbon in Molten Slags

机译：碳在熔渣中的热力学行为

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The solubility of carbon in the MO-B_2O_3 (MO = CaO, BaO, and NA_2O) and CaO-RO (RO = SiO_2 and Al_2O_3) slags at high temperatures was measured to understand the thermodynamic behavior of carbon in molten slags. The solubility of carbon as a function of the composition of slags shows a minimum value, indicating that carbon dissolves by different mechanisms in the acidic and basic slags, respectively. The infrared spectra measurements indicate that the B-C bond is about 1150 and 1140 cm~(-1) in the acidic region of the CaO-B_2O_3 and Na_2O-B_2O_3 slags; hence, the incorporation of carbon into the borate network is confirmed qualitatively. The dissolution of carbon and nitrogen into the slags shows a similar behavior in the B_2O_3-bearing slags, while the different behavior is shown in the CaO-SiO_2 an CaO-Al_2O_3 slags, based on the relationship between carbide capacity and nitride capacity.
机译：测量了碳在高温下在MO-B_2O_3（MO = CaO，BaO和NA_2O）和CaO-RO（RO = SiO_2和Al_2O_3）炉渣中的溶解度，以了解碳在熔渣中的热力学行为。碳作为炉渣成分的函数的溶解度显示出最小值，表明碳分别通过不同的机理溶解在酸性和碱性炉渣中。红外光谱测量表明，CaO-B_2O_3和Na_2O-B_2O_3炉渣的酸性区域中B-C键分别为1150和1140 cm〜（-1）。因此，定性地证实了碳向硼酸盐网络中的结合。根据碳化物容量和氮化物容量之间的关系，在含B_2O_3-的炉渣中碳和氮的溶解表现出相似的行为，而在CaO-SiO_2和CaO-Al_2O_3炉渣中表现出不同的行为。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号