Single-crystal whiskers of R_1Ba_2Cu_3O_x (R-123, R = La, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb and Lu) phase have been successfully grown by the Te- and Ca-doping method. The whiskers were grown from precursor pellets at just below their partial melting (peritectic) temperatures. The nominal composition of the R-123 whiskers is R_(1-u),Ba_(2-v),Ca_wCu_3O_x (u + v + w = 0, w > 0) with R and/or Ba sites being substituted by Ca. However, the amount of Te was less than the analytical limit. The critical temperatures of the R-123 whiskers were around 80 K, and among these whiskers those with larger R ionic radii such as Dy, Gd, Eu and Sm require post-annealing in an oxygen atmosphere.
机译：R_1Ba_2Cu_3O_x（R-123，R = La，Nd，Sm，Eu，Gd，Dy，Ho，Er，Tm，Yb和Lu）相的单晶晶须已通过Te和Ca掺杂方法成功生长。晶须是由前体颗粒在低于其部分熔融（包晶）温度下生长的。 R-123晶须的标称成分为R_（1-u），Ba_（2-v），Ca_wCu_3O_x（u + v + w =​​ 0，w> 0），其中R和/或Ba位被Ca取代。但是，Te量小于分析极限。 R-123晶须的临界温度约为80 K，在这些晶须中，那些具有较大R离子半径（例如Dy，Gd，Eu和Sm）的晶须需要在氧气气氛中进行后退火。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号