摘要

The growth of AIN rod-like crystals, successfully produced via direct nitridation of Al-alloy doped with 5 wt% Mg and 2 wt% Si at 1273 K is predominantly based on capillary niass-transfer phenomena, which occur through a network of micro-channels developed in the empty space among the AIN columnar crystals as well as the hollows inside these crystals. The diffusion of N-2 in the liquid alloy is the rate-determining step of the process. Mg and Mg3N, resulting after nitridation maintain a very low partial pressure of oxygen during the entire process and favour the formation of AIN. (c) 2005 Elsevier B.V. All rights reserved.
机译：AIN棒状晶体的生长是通过在1273 K处对掺有5 wt％Mg和2 wt％Si的铝合金进行直接氮化而成功产生的，这主要是基于毛细管的镍传输现象，这种现象是通过微网络形成的。在AIN柱状晶体之间的空隙以及这些晶体内部的空洞中形成了通道。 N-2在液态合金中的扩散是该过程的决定速率的步骤。氮化后生成的Mg和Mg3N在整个过程中保持非常低的氧分压，有利于AIN的形成。 （c）2005 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号