首页> 外文期刊>Journal of Iron and Steel Research International >Formation of ZrB_2 in MgO-C Composite Materials Using In-Situ Synthesis Method
【24h】

Formation of ZrB_2 in MgO-C Composite Materials Using In-Situ Synthesis Method

机译：原位合成法在MgO-C复合材料中形成ZrB_2

获取原文
获取原文并翻译 | 示例
       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

ZrB_2 in MgO-C composite materials obtained by both microwave sintering synthesis and in-situ reaction at lower temperature was investigated. The test result shows that 66. 67 percent of reactant changed into ZrB_2, and the other form Al_2O_3, which could optimize the properties of carbon-containing materials. Therefore, the method of in-situ synthesizing ZrB_2 acting as antioxidant in carbon-containing materials is considered as one of best ways to reduce the cost and ZrB_2 as refractories is used on a large-scale.
机译：研究了微波烧结合成和低温原位反应制得的MgO-C复合材料中的ZrB_2。测试结果表明，有66.67％的反应物变为ZrB_2，而另一种形式为Al_2O_3，可以优化含碳材料的性能。因此，原位合成含碳材料中作为抗氧化剂的ZrB_2的方法被认为是降低成本的最佳方法之一，并且作为耐火材料的ZrB_2被大量使用。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号