首页> 外文期刊>Journal of Iron and Steel Research International >Dynamic Recrystallization Behavior in Mn-Cr Gear Steel
【24h】

Dynamic Recrystallization Behavior in Mn-Cr Gear Steel

机译：Mn-Cr齿轮钢的动态再结晶行为

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Using a Gleeble 1500 hot simulator, the dynamic recrystallization (DRX) behavior of Mn-Cr type gear steel was investigated. The experimental results show that the Mn-Cr gear steel exhibits a typical DRX behavior at higher deformation temperature, lower strain rate and smaller initial austenite grain size. The DRX takes place under the conditions that Zener-Hollomon parameter (Z) is less than a critical value Z_c. The DXR grains are formed by the bulging mechanism. Activation energy and stress exponent were calculated to be 378.6 kJ centre dot mol~(-1) and 5.8 respectively by regression analysis.
机译：使用Gleeble 1500热模拟器，研究了Mn-Cr型齿轮钢的动态重结晶（DRX）行为。实验结果表明，Mn-Cr齿轮钢在较高的变形温度，较低的应变速率和较小的初始奥氏体晶粒尺寸下表现出典型的DRX行为。在齐纳-所罗门参数（Z）小于临界值Z_c的条件下进行DRX。 DXR晶粒是通过鼓胀机制形成的。回归分析得出活化能和应力指数分别为378.6 kJ中心点mol〜（-1）和5.8。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号