首页> 外文期刊>Journal of nano research >Hot Injection Synthesis of Orthorhombic SnS Nanoparticies from Bis(O-N-Propyldithiocarbonato)Diphenyltin(Ⅳ)
【24h】

Hot Injection Synthesis of Orthorhombic SnS Nanoparticies from Bis(O-N-Propyldithiocarbonato)Diphenyltin(Ⅳ)

机译：双晶体SNS纳米颗粒的热注射合成来自双（O-N-丙炔烃）二苯基锡（Ⅳ）

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The bis (O-n-propyldithiocarbonato) diphenyl of tin (IV) [Ph_(2)Sn (S_(2)CO~(n)Pr)_(2)] was synthesized as a precursor for the preparation of SnS nanoparticles. The complex was characterized by X-ray single crystal diffraction, thermogravimetric analyses (TGA), nuclear magnetic resonance (NMR) and IR spectroscopy. Hot injection method was used to synthesize the SnS nanoparticles under nitrogen atmosphere at 260 °C. The SnS nanoparticles formed were studied by powder X-ray diffraction, Raman spectroscopy and transmission electron microscopy (TEM). The phase was found to be polycrystalline, orthorhombic SnS with a strong (111) preferred orientation. The band gap of SnS nanoparticles is 1.28eV.
机译：合成的锡（IV）[pH_（2）Sn（S_（2）CO〜（N）] _（2）]作为制备SNS纳米颗粒的前体，合成双（O-N-丙炔二硫代甲苯胺）二苯基。该复合物的特征在于X射线单晶衍射，热重分析（TGA），核磁共振（NMR）和IR光谱。使用热注射方法在260℃下在氮气氛下在氮气氛下合成SNS纳米颗粒。通过粉末X射线衍射，拉曼光谱和透射电子显微镜（TEM）研究形成的SNS纳米粒子。发现该相是多晶，正交的Sn，具有强（111）优选的取向。 SNS纳米粒子的带隙为1.28EV。