A polysulfide electrolyte considering simultaneously the penetration of the electrolyte in a mesoscopic TiO_2 film and the ion dissociation in the solution is developed for application in a CdS-sensitized solar cell (CdS-DSSC). A methanol/water (7:3 by volume) solution was found to be a good solvent for fitting the requirement mentioned above. The optimal composition of the electrolyte, based on the performance of the CdS-DSSCs, was found to contain 0.5 M Na_2S, 2 M S, and 0.2 M KCl. By using a photoelectrode prepared after 4 cycles of chemical bath deposition, FTO/TiO2/CdS-4, the efficiency of the CdS-DSSC obtained for this polysulfide electrolyte is 1.15% under the illumination of 100% sun (AM1.5,100 mW cm~(-2)). This efficiency is less than that obtained using I~-/I_3~- redox couple (1.84%), mainly caused from the smaller values of fill factor and open circuit potential. However, the CdS sensitizer is stable and, furthermore, a much higher short circuit current and IPCE (80%) are obtained by using the polysulfide electrolyte.
机译：开发了一种同时考虑电解质在介观的TiO_2膜中的渗透和溶液中离子的离解的多硫化物电解质，用于CdS敏化太阳能电池（CdS-DSSC）。发现甲醇/水（体积比为7：3）是满足上述要求的良好溶剂。基于CdS-DSSC的性能，发现电解质的最佳组成包含0.5 M Na_2S，2 M S和0.2 M KCl。通过使用经过4个化学浴沉积循环后制备的光电极FTO / TiO2 / CdS-4，在100％的太阳光照下（AM1.5,100 mW cm〜 （-2））。该效率低于使用I〜-/ I_3〜-氧化还原对所获得的效率（1.84％），这主要是由于填充系数和开路电势的值较小所致。然而，CdS敏化剂是稳定的，此外，通过使用多硫化物电解质获得了更高的短路电流和IPCE（80％）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号