首页> 外文期刊>Key Engineering Materials >Influence of 3Y-TZP on Microstructure and Mechanical Properties of Al_2O_3-based Composites
【24h】

Influence of 3Y-TZP on Microstructure and Mechanical Properties of Al_2O_3-based Composites

机译：3Y-TZP对Al_2O_3基复合材料组织和力学性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Al_2O_3 composites with different volume fractions of 3Y-TZP (3 mol% yttria-doped tetragonal zirconia polycrystalline) were prepared by using a colloidal process and pressure-casting into green specimens, then were pressureless sintered to full density at 1550℃. The resulted two-phase microstructure contained uniformly distributed and submicro- meter-sized grains. The addition of 15 vol% ZrO_2 resulted in an increase in bending strength (average 656 MPa by 4 pt. test). Appreciate amount of m-ZrO_2 phase was detected after fracture. The enhanced transformability results in an increase in flexural strength and toughness. The addition of 30 vol% ZrO_2 resulted in best toughness (5.4 MPam~(0.5)) and outstanding wear resistance (7.2 × 10~(-8) cm~3/Nm).
机译：采用胶体工艺制备了不同体积分数的3Y-TZP（3 mol％氧化钇掺杂的四方氧化锆多晶）Al_2O_3复合材料，并压铸成绿色试样，然后在1550℃无压烧结至全密度。产生的两相组织包含均匀分布的亚微米级晶粒。添加15 vol％的ZrO_2导致抗弯强度增加（4磅测试平均656 MPa）。断裂后检测到适量的m-ZrO_2相。增强的可变形性导致弯曲强度和韧性的增加。加入30％（体积）的ZrO_2可获得最佳的韧性（5.4 MPam〜（0.5））和出色的耐磨性（7.2×10〜（-8）cm〜3 / Nm）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号