首页> 外文期刊>Materials Letters >Microstructural properties of M_7C_3 eutectic carbides in a Fe-Cr-C alloy
【24h】

Microstructural properties of M_7C_3 eutectic carbides in a Fe-Cr-C alloy

机译：Fe-Cr-C合金中M_7C_3共晶碳化物的显微组织性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The microstructure of Fe-Cr-C coatings was investigated with optical microscope (OP), scanning electron microscope (SEM), electron dispersive spectrograph (EDS), respectively. The coatings were formed by means of gas tungsten arc welding method on the AISI 4340 steel. The microstructures of the coatings are found to compose of primary M_7C_3 carbides in eutectic of austenite matrix. The hypereutectic microstmcture consisted of M_7C_3 and M_7C_3 + austenite (gamma). The hardness values of M_7C_3 carbides varied between 1050 and 1500 HV, while the hardness of M_7C_3+austenite (gamma) matrix measured between 500 and 750 HV. The lower hardness of matrix of the coating microstmcture was related to the relatively low concentrations of Cr and C.
机译：用光学显微镜（OP），扫描电子显微镜（SEM），电子分散光谱仪（EDS）研究了Fe-Cr-C涂层的微观结构。涂层是通过气体钨极电弧焊法在AISI 4340钢上形成的。发现涂层的微观结构由奥氏体基体的共晶中的主要M_7C_3碳化物组成。过共晶组织由M_7C_3和M_7C_3 +奥氏体（γ）组成。 M_7C_3碳化物的硬度值在1050和1500 HV之间变化，而M_7C_3 +奥氏体（γ）基体的硬度在500和750 HV之间测量。涂层显微组织的较低硬度与Cr和C的相对较低浓度有关。

著录项

  • 来源
    《Materials Letters》 |2006年第5期|p.605-608|共4页
  • 作者

    S. Buytoz;

  • 作者单位

    University of Firat, Faculty of Technical Education, Department of Metallurgy, 23119 Elazig, Turkey;

  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 工程材料学;
  • 关键词

    M_7C_3 carbides; Retained austenite; Coating;

    机译：M_7C_3碳化物;残余奥氏体;涂层;