Stimulated emission from microcrystalline CsPbBr_3 films is measured under several excitation/detection geometries including the measurements of optical gain. Threshold for stimulated emission is strongly dependent on the geometries. In particular, in the stripe-shape excitation geometry, the edge luminescence is, unlike the case for the simultaneously measured surface luminescence, solely composed of stimulated emission even for a very low excitation fluence of a few kW/cm~2, suggesting a very low threshold for the stimulated emission. The net optical gain at 77 K amounted to 130cm~(-1) at 32kW/cm~2 excitation fluence and increased up to 300 cm~(-1) at 210kW/cm~2.
机译：在几种激发/检测几何结构（包括光学增益的测量）下测量微晶CsPbBr_3膜的受激发射。受激发射的阈值在很大程度上取决于几何形状。特别是，在条形激发几何结构中，与同时测量的表面发光不同，边缘发光仅由受激发射组成，即使对于几千瓦/ cm〜2的非常低的激发通量也是如此。受激发射的低阈值。在32kW / cm〜2激发通量下，在77 K下的净光学增益为130cm〜（-1），在210kW / cm〜2下的净光学增益增加至300cm〜（-1）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号