首页> 外文期刊>Revista de metalurgia >Electron microscopy characterization of mechanically alloyed and hot consolidales Cu-Cr_3C_2 particles
【24h】

Electron microscopy characterization of mechanically alloyed and hot consolidales Cu-Cr_3C_2 particles

机译：机械合金化和热固结的Cu-Cr_3C_2粒子的电子显微镜表征

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Se obtuvieron, aleaciones compuestas de Cu-Cr_3C_2, aleadas mecanicamente, para estudiar futuras aplicaciones en componentes electricos. A altas temperaturas, las aleaciones de base cobre reforzadas por dispersion, son atractivas por su excelente conductividad termica y electrica, propiedades mecanicas y estabilidad microstructural. En este estudio, mezclas de polvo de cobre puro con un 2 percent en vol. de Cr_3C_2, obtenidas mediante molienda en un molino de bolas planetario de alta energia, durante 4, 6, 10, 12 y 15 h, se compactaron isostaticamente en caliente a 1.073 K durante 2 h con una presion de 100 MPa en argon, para obtener un material con una microestructura fina. Las aleaciones de Cu-Cr_3C_2 se estudiaron, mediante microscopia electronica de barrido MEB y de transmision MET, ademas de microsonda electronica. Tambien, se caracterizaron las propiedades mecanicas y la conductividad electrica, obteniendose valores de 500 MPa y 50 percent IACS, respectivamente. Las ceramicas de Cr_3C_2 presentan una buena estabilidad durante la compactacion en caliente. Se observo la precipitacion de particulas de tamano nanometrico en la matriz de cobre, consistentes en carburos de hierro precipitados en ella, lo que contribuye al reforzamiento adicional de estas aleaciones. Los oxicarburos de Fe-Cr, formados en la interfase entre particulas de Cr_3C_2 y la matriz de cobre provocan la baja ductilidad de estas aleaciones. Estas particulas son atribuibles a impurezas y contaminacion generada durante el proceso de molienda.%Mechanically alloyed copper-ceramic composites have been obtained with the purpose of studying their use as copper-based material for electrical equipment. For high-temperature applications, dispersion-strengthened copper alloys are attractive due to their excellent combination of thermal and electrical conductivity, mechanical strength retention and microstructural stability. In this work, powder mixtures of pure copper with 2 vol percent Cr_3C_2, milled during 4, 6, 10, 12 and 15 h in a high-energy planetary balls mill under argon atmosphere, were consolidated by hot isostatic pressing, applying a pressure of 100 MPa at 1073 K for two hours, to obtain materials with a fine microstructure. The Cu-Cr_3C_2 alloys were studied by scanning electron microscopy (SEM), electron microprobe (EPMA) and transmission electron microscopy (TEM). Mechanical properties and electrical conductivity were also studied. The average tensile strength and electrical conductivity were found to be 500 MPa and 50 percent IACS, respectively. The Cr_3C_2 ceramics show good stability during hot consolidation. Contributing to a further strengthening of the alloy during the hot consolidation, uniformly-distributed Fe-carbide particles of nanometric size precipitated in the copper matrix. Fe-Cr oxycarbides formed in the interphase between Cr_3C_2 particles and the copper matrix cause the low ductility of Cu-Cr_3C_2 alloys. Said particles are attributed to impurities/contamination generated from the milling process.
机译：获得了机械合金化的Cu-Cr_3C_2复合合金，以研究电气元件的未来应用。在高温下，弥散增强铜基合金因其出色的导热性和导电性，机械性能和微观结构稳定性而具有吸引力。在这项研究中，纯铜粉与2％（体积）的混合物。在高能行星式球磨机中研磨得到的Cr_3C_2的4、6、10、12和15 h，在氩气中以100 MPa的压力在1,073 K下热等静压2 h，以获得具有良好微观结构的材料。除电子显微探针外，还通过扫描电子显微镜MEB和透射MET研究了Cu-Cr_3C_2合金。此外，还对机械性能和电导率进行了表征，分别获得了500 MPa和50％IACS的值。 Cr_3C_2陶瓷在热压过程中具有良好的稳定性。观察到纳米颗粒在铜基质中的沉淀，该沉淀由在其中沉淀的碳化铁组成，这有助于这些合金的额外增强。在Cr_3C_2颗粒和铜基体之间的界面处形成的Fe-Cr碳氧化合物导致这些合金的延展性较低。这些颗粒归因于在研磨过程中产生的杂质和污染。为了研究将其用作电气设备的铜基材料，已经获得了机械合金化的铜陶瓷复合材料。对于高温应用，分散增强的铜合金具有极好的导热和导电性，机械强度保持性和微观结构稳定性，因此具有吸引力。在这项工作中，在氩气气氛下于高能行星球磨机中于4、6、10、12和15小时内研磨的纯铜和2％Cr_3C_2的粉末混合物，通过热等静压进行固结，压力为在1073 K的压力下，在100 MPa的压力下进行两个小时，以获得具有良好微观结构的材料。通过扫描电子显微镜（SEM），电子探针（EPMA）和透射电子显微镜（TEM）研究了Cu-Cr_3C_2合金。还研究了机械性能和电导率。发现平均抗拉强度和电导率分别为500 MPa和50％IACS。 Cr_3C_2陶瓷在热固结过程中表现出良好的稳定性。在热固结过程中，有助于进一步强化合金，纳米尺寸的均匀分布的碳化铁颗粒沉淀在铜基质中。在Cr_3C_2颗粒与铜基体之间的相中形成的Fe-Cr碳氧化物导致Cu-Cr_3C_2合金的延展性低。所述颗粒归因于研磨过程中产生的杂质/污染。