首页> 外文期刊>Organic Electronics >Photovoltaic cells from a soluble pentacene derivative
【24h】

Photovoltaic cells from a soluble pentacene derivative

机译：可溶性并五苯衍生物的光伏电池

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Multilayer heterojunction photovoltaic cells were fabricated using a solution processable pentacene derivative as the donor layer. Upon annealing of these devices, the open circuit voltage was found to gradually increase with temperature up to 265 degrees C. Further improvement in the photovoltaic performance was achieved with the incorporation of mobile ions into the donor material for concentrations of lithium triflate up to 1.4 mg/ml. Finally, after introducing an exciton blocking layer, an optimized white-light (100 mW/cm(2)) power conversion efficiency of 0.52% was achieved. (C) 2006 Elsevier B.V. All rights reserved.
机译：使用可溶液加工的并五苯衍生物作为供体层来制造多层异质结光伏电池。在对这些器件进行退火后，发现开路电压会随着温度升高至265摄氏度而逐渐增加。通过将供体材料中的三氟甲磺酸锂浓度高达1.4 mg的移动离子掺入施主材料中，实现了光伏性能的进一步改善。 /毫升。最后，在引入激子阻挡层之后，获得了优化的白光（100 mW / cm（2））转换效率为0.52％。 （C）2006 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号