首页> 外文期刊>Solid State Communications >Physical property characterization of Fe-tube encapsulated and vacuum annealed bulk MgB2
【24h】

Physical property characterization of Fe-tube encapsulated and vacuum annealed bulk MgB2

机译：铁管封装和真空退火的块状MgB2的物理性质表征

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We report the phase formation, and present a detailed study of magnetization and resistivity under magnetic field of MgB2 polycrystalline bulk samples prepared by the Fe-tube encapsulated and vacuum (10(-5) Torr) annealed (750 degrees C) route. Zero-field-cooled magnetic susceptibility (chi(ZFC)) measurements exhibited a sharp transition to the superconducting state with a sizeable diamagnetic signal at 39 K (T-c). The measured magnetization loops of the samples, despite the presence of flux jumps, exhibited a stable current density (J(c)) of around 2.4 x 10(5) A/cm(2) in up to 2 T (Tesla) field and at temperatures (T) up to 10 K. The upper critical field is estimated from resistivity measurements in various fields and shows a typical value of 8 T at 21 K. Further, chi(FC) measurements at an applied field of 0.1 T reveal a paramagnetic Meissner effect (PME) that is briefly discussed. (c) 2006 Elsevier Ltd. All rights reserved.
机译：我们报告相的形成，并提出了磁场下的磁化和电阻率的详细研究MgB2多晶大块样品通过铁管封装和真空（10（-5）托）退火（750摄氏度）路线制备的。零场冷却的磁化率（chi（ZFC））测量显示出在39 K（T-c）处具有较大的反磁信号时会急剧过渡到超导状态。尽管存在磁通跳跃，但所测得的样品的磁化回路在高达2 T（Tesla）的磁场中仍表现出大约2.4 x 10（5）A / cm（2）的稳定电流密度（J（c））和在高达10 K的温度（T）下。根据各个领域的电阻率测量值估算出上临界场，该临界场在21 K下的典型值为8T。此外，在0.1 T的施加场下的chi（FC）测量表明，简要讨论了顺磁迈斯纳效应（PME）。 （c）2006 Elsevier Ltd.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号