首页> 外文期刊>Solid State Communications >Synthesis of crystalline SrMoO4 nanowires from polyoxometalates
【24h】

Synthesis of crystalline SrMoO4 nanowires from polyoxometalates

机译：由多金属氧酸盐合成晶体SrMoO4纳米线

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Crystalline SrMoO4 nanowires were synthesized via a facile hydrothermal process at 180 degrees C for 10h.alpha-(NH4)(6)-P(2)Mo(18)O(62)center dot nH(2)O one of polyoxometalates with Dawson structure, was employed as the source of molybdates. The diameter and length of the obtained SrMoO4 nanowires are about 20 nm and 5-10 mu m, respectively. HRTEM results show that the SrMoO4 nanowires are of high crystallinity with rough surface. However, when Na(2)MoO(4)center dot 2H(2)O was used, there are only SrMoO4 nanorods with smaller aspect ratio (200/70 nm) in the similar hydrothermal process. The probable growth mechanism was discussed. (c) 2005 Elsevier Ltd. All rights reserved.
机译：结晶SrMoO4纳米线是通过在180摄氏度下进行10h的水热合成过程合成的。结构，被用作钼酸盐的来源。所获得的SrMoO 4纳米线的直径和长度分别为约20nm和5-10μm。 HRTEM结果表明，SrMoO4纳米线结晶度高，表面粗糙。但是，当使用Na（2）MoO（4）中心点2H（2）O时，在类似的水热过程中只有纵横比较小（200/70 nm）的SrMoO4纳米棒。讨论了可能的增长机制。 （c）2005 Elsevier Ltd.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号