首页> 外文期刊>Solid State Communications >Competing magnetic interactions in Dy1-xSmxFe10Si2 compounds
【24h】

Competing magnetic interactions in Dy1-xSmxFe10Si2 compounds

机译：Dy1-xSmxFe10Si2化合物中竞争的磁相互作用

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The spin reorientation temperatures of Dy1-x SmxFe10Si2 compounds with x=0, 0.1, 0.2, 0.3, 0.4, 0.6 and 1.0 were investigated using dc magnetization measurements in the temperature range from 5 to 350 K. The spin reorientation (SR) temperature was observed to drop gradually from 255 to 52 K as Sm content was increased from x=0 to 0.4. No SR temperature was observed for x > 0.4. Magnetization measurements using vibrating sample magnetometry (VSM) were carried out from room temperature to 650 K to determine the dependence of the Curie temperature on Sm content. The Curie temperatures shifted to higher values as the Sm content was increased. X-ray powder diffraction studies revealed that the substitution of Sm for Dy leads to an increase in the lattice parameter a and the unit cell volume V while the lattice parameter c remained constant. (C) 2005 Elsevier Ltd. All rights reserved.
机译：使用dc磁化测量在5至350 K的温度范围内研究了x = 0、0.1、0.2、0.3、0.4、0.6和1.0的Dy1-x SmxFe10Si2化合物的自旋重取向温度。当Sm含量从x = 0增加到0.4时，可观察到从255逐渐下降到52K。 x> 0.4时未观察到SR温度。使用振动样品磁力法（VSM）从室温到650 K进行磁化测量，以确定居里温度对Sm含量的依赖性。随着Sm含量的增加，居里温度转变为更高的值。 X射线粉末衍射研究表明，Sm替代Dy导致晶格参数a和晶胞体积V增大，而晶格参数c保持恒定。 （C）2005 Elsevier Ltd.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号