The mechanical properties of Fe-36.5/100 Al (mole fraction) intermetallic alloy at elevated temperatures were measured. The results indicate that the specific elongation of the alloy increases significantly with the temperature increasing from 600 deg. C to 1000 deg. C and the maximum of specific elongation is up to 115/100 when the alloy is deformed at 1000 deg. C. The dislocation features in the alloy were also investigated by transmis- sion electron microscopy (TEM). There exist not only a large number of gliding dislocation lines but also a number of helical dislocations in FeAl alloy after deformed at elevated temperatures.
机译：测量了Fe-36.5 / 100 Al（摩尔分数）金属间合金在高温下的力学性能。结果表明，合金的比伸长率随温度从600℃升高而显着增加。摄氏度到1000度C，当合金在1000度下变形时，比伸长率的最大值高达115/100。 C.还通过透射电子显微镜（TEM）研究了合金中的位错特征。 FeAl合金在高温下变形后不仅存在大量的滑动位错线，而且还存在许多螺旋位错。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号