摘要

A novel linear polymer (PFABT) containing bithiazole rings was synthesized by polycondensation of 2,2'-diamino-4,4'-bithiazole (DABT) and formaldehyde. The complexes of PFABT with two transition metal ions (Fe{sup}(2+), Cu{sup}(2+)) were prepared for the first time. The polymer was determined through FT-IR, 1{sup left}H-NMR and elemental analysis (EA), and the complexes were characterized by FT-IR. The magnetic behaviors of these complexes were measured as a function of magnetic field strength (0-50 kOe) at 4K and as a function of temperature (4-300 K) under an applied magnetic field of 30 kOe. The results show that PFABT-Cu{sup}(2+) is a ferromagnet while PFABT-Cu{sup}(2+) is an anti-ferromagnet.
机译：通过2,2'-二氨基-4,4'-Bithiazole（DABT）和甲醛的缩聚反应合成了一种新型的含有Bithiazole环的线性聚合物（PFABT）。首次制备了PFABT与两种过渡金属离子（Fe {sup}（2 +），Cu {sup}（2+））的配合物。通过FT-IR，1 H-NMR和元素分析（EA）测定聚合物，并通过FT-IR表征该配合物。在30 kOe的施加磁场下，这些配合物的磁性行为是作为4K时的磁场强度（0-50 kOe）和温度（4-300 K）的函数来测量的。结果表明，PFABT-Cu {sup}（2+）是铁磁体，而PFABT-Cu {sup}（2+）是反铁磁体。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号