摘要

The pyrotechnic and thermal properties of a range of binary magnesium-strontium nitrate compositions containing from 10% to 90% by mass of magnesium have been determined.The burning rate and light output were measured after consolidating the compositions into cardboard tubes.The exothermicity,temperature of ignition and time to ignition of the compositions were also determined and the products of combustion were characterized.The compositions were found to burn reliably over the range 20% to 70% magnesium.The composition containing 70% magnesium was found to have the maximum burning rate and light output,while the maximum exothermicity was observed at 40% magnesium.The temperature and times of ignition decreased as the magnesium content was increased to 40% and thereafter did not change significantly.
机译：测定了一系列镁含量为10％至90％的二元硝酸镁锶锶组合物的烟火学和热学性质。将组合物固结到纸板管中后测量其燃烧速率和光输出。放热度，温度还确定了组合物的着火时间和着火时间并表征了燃烧产物。发现该组合物在20％至70％的镁范围内可靠地燃烧。发现含有70％的镁的组合物具有最大的燃烧在40％的镁下观察到最大放热率。随着镁含量增加到40％，点火的温度和次数减少，此后没有明显变化。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号