Ba doped PLZT ceramic compositions with formula Pb0.982-zLa0.012 Delta Ba-0.006(z)( Zr0.55Ti0.45) O-3 for z = 0 to 6 mole% are synthesized by mixed-oxide method. Powder XRD studies indicate the coexistence of rhombohedral and tetragonal phase in 5 mole% Ba doped PLZT composition. SEM pictures show grain size control as Ba concentration increases in PLZT system. epsilon(rt) and tan delta are increased up to 4 mole% and 5 mole% Ba doped PLZT composition respectively. Dielectric maximum ( epsilon(TC)) is decreased to 4 mole% Ba doped PLZT and Curie temperature (T-C) is decreased with increase of Ba concentration in PLZT system. Coercive field (E-c) has shown gradual enhancement over series. Remanent (P-r) and spontaneous (P-s) polarizations are decreased to 5 mole% Ba doped PLZT composition.
机译：通过混合氧化物法合成具有z为0至6摩尔％的式Pb0.982-zLa0.012δBa-0.006（z）（Zr0.55Ti0.45）O-3的Ba掺杂PLZT陶瓷组合物。粉末XRD研究表明，在5摩尔％Ba掺杂的PLZT组合物中，菱面相和四方相共存。 SEM照片显示PLZT系统中随着Ba浓度的增加而进行晶粒尺寸控制。 epsilon（rt）和tanδ分别增加到掺杂Ba的PLZT成分的4摩尔％和5摩尔％。随着PLZT系统中Ba浓度的增加，介电最大值（ε）降低至4摩尔％Ba掺杂的PLZT，居里温度（T-C）降低。矫顽场（E-c）已显示出逐渐增强的序列。剩余极化（P-r）和自发极化（P-s）降低到掺杂Ba的PLZT成分为5摩尔％。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号