首页> 外文期刊>Carbohydrate Polymers: Scientific and Technological Aspects of Industrially Important Polysaccharides >Regenerated cellulose fibers spun-dyed with carbon black/latex composite dispersion
【24h】

Regenerated cellulose fibers spun-dyed with carbon black/latex composite dispersion

机译：炭黑/乳胶复合分散体纺制的再生纤维素纤维

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A carbon black (CB)/Iatex composite was prepared by the method of miniemulsion polymerization for use as a colorant for spun dyeing of regenerated cellulose fibers. Analysis of experimental results revealed that the CB/latex composite had a small particle size and a narrow particle size distribution which were important to ensure a stable dispersion being later added to spinning solution. A good stability of the prepared CB/latex composite dispersion in the spinning solution indicated that it was highly possible to use the CB/latex composite as a colorant for spun dyeing of regenerated cellulose fibers. When a 3.5% mass ratio of CB/latex composite to cellulose was used for spun dyeing, the spun-dyed fibers had the highest tensile strength, breaking elongation and color strength. The rubbing and washing color fastnesses of spun-dyed regenerated cellulose fibers could satisfy requirements of most textiles. This study provided a new insight into producing spun-dyed regenerated cellulose with a novel colorant.
机译：通过细乳液聚合的方法制备炭黑（CB）/ Iatex复合材料，用作再生纤维素纤维的纺丝染色的着色剂。对实验结果的分析表明，CB /胶乳复合物具有小的粒径和窄的粒径分布，这对于确保随后将稳定的分散体添加到纺丝溶液中是重要的。所制备的CB /乳胶复合物在纺丝溶液中的良好稳定性表明，非常有可能将CB /乳胶复合物用作用于再生纤维素纤维的染色的着色剂。当将CB /胶乳复合材料与纤维素的质量比为3.5％用于纺丝染色时，纺丝染色的纤维具有最高的拉伸强度，断裂伸长率和色强度。纺制的再生纤维素纤维的摩擦和水洗色牢度可以满足大多数纺织品的要求。这项研究为使用新型着色剂生产纺粘再生纤维素提供了新的见解。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号