首页> 外文期刊>Wire Journal International >Investigations of the aging process of high carbon steel spring wires
【24h】

Investigations of the aging process of high carbon steel spring wires

机译：高碳钢弹簧线的时效过程研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Three conclusions were reached from the research presented in this paper. They are as follows: Research results confirmed literature data concerned with variations of tensile strength R_m and number of twists N_t of drawn wires in a result of aging after drawing. New parameter W_t defined as a ratio of tensile strength R_m to number of twists N_t is very sensitive for estimation of the effect of aging for properties of wires with a diameter 0.9 mm. 3) For considered steels it is possible to predict tensile strength R_m and number of twists N_t of wires after assumed period of aging and relations of ratio "W_t" to the carbon content.
机译：本文提出的研究得出了三个结论。它们如下：研究结果证实了与拉伸后的时效导致的拉伸线的抗拉强度R_m和捻数N_t的变化有关的文献数据。被定义为抗拉强度R_m与捻数N_t之比的新参数W_t对于估计直径为0.9mm的电线的特性的老化影响非常敏感。 3）对于考虑中的钢，可以在假定的时效周期和“ W_t”与碳含量的关系之后，预测抗拉强度R_m和钢丝的捻数N_t。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号