首页> 外文期刊>Chinese science bulletin >Synthesis and pervaporation performance of high-reproducibility silicalite-1 membranes
【24h】

Synthesis and pervaporation performance of high-reproducibility silicalite-1 membranes

机译：高重现性silicalite-1膜的合成和全蒸发性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

High-reproducibility silicalite-1 membranes were synthesized on silica tubes by in-situ hydrothermal synthesis, and the relative standard deviation (R.S.D.) of average separation factor for eight membranes was only 7.5%. By using an effective method called "solution-filling (SF)", the average flux of membranes prepared with SF method was improved by about 49% compared to membranes prepared without SF method, and the highest flux of membrane prepared with SF method towards ethanol/H2O mixture at 80 degrees C was 1.49 kg/(m(2)center dot h). Pervaporation experiments showed that the fluxes of silicalite-1 membranes at 60 degrees C were 2.63, 0.87, 0.24, and 0.20 kg/(m(2)center dot h) towards methanol/H2O, ethanol/H2O, 2-propanol/H2O, and 1-propanol/H2O mixtures, respectively, and the corresponding separation factors were 22, 69, 81, and 159, respectively.
机译：通过原位水热合成在硅胶管上合成了高重现性的silicalite-1膜，八种膜的平均分离系数的相对标准偏差（R.S.D.）仅为7.5％。通过使用一种称为“溶液填充（SF）”的有效方法，与不使用SF方法制备的膜相比，使用SF方法制备的膜的平均通量提高了约49％，并且使用SF方法制备的膜对乙醇的通量最高。 / H2O混合物在80摄氏度下为1.49千克/（m（2）中心点h）。全蒸发实验表明，silicalite-1膜在60摄氏度时通向甲醇/ H2O，乙醇/ H2O，2-丙醇/ H2O的通量为2.63、0.87、0.24和0.20 kg /（m（2）中心点h），和1-丙醇/ H2O混合物的分离系数分别为22、69、81和159。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号