The Combined Loading Compression (CLC) test method was standardized by ASTM in 2001, as ASTM D6641. During the past 10 years it has become the most-used compression test method for composite materials. The principal reasons for its popularity are the efficiency of load introduction into the specimen and the simplicity and ease of use of the test fixture. ASTM standardized the fixture size and configuration shown at the center of Fig. 1, flanked by two nonstandard-size fixtures. The standard fixture accommodates a specimen 140-mm/5.5-inches long with a gage section length of 13 mm/0.5 inch. Although the standard fixture will accommodate a specimen up to 30-mm/1.2-inches wide, a 13-mm/0.5-inch specimen width is most common. This specimen's overall length, gage length and width are the same as those typically used with the ASTM D3410 compression test method2 and represent a practical compression specimen size.
机译：组合载荷压缩（CLC）测试方法由ASTM于2001年标准化，称为ASTM D6641。在过去的十年中，它已成为复合材料最常用的压缩测试方法。其普及的主要原因是负载引入样品的效率高以及测试夹具的简单易用。 ASTM标准化了图1中心所示的灯具尺寸和配置，两侧是两个非标准尺寸的灯具。标准夹具可容纳140毫米/5.5英寸长的标本，标距截面长度为13毫米/0.5英寸。尽管标准夹具最多可容纳30毫米/1.2英寸宽的样本，但最常见的样本宽度是13毫米/0.5英寸。该样品的总长度，量规长度和宽度与ASTM D3410压缩测试方法2通常使用的相同，代表实际的压缩样品尺寸。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号