首页> 外文期刊>Zeitschrift fur Anorganische und Allgemeine Chemie >Na_3SbSe_3: Synthesis, crystal structure determination, raman spectroscopy, and ionic conductivity
【24h】

Na_3SbSe_3: Synthesis, crystal structure determination, raman spectroscopy, and ionic conductivity

机译：Na_3SbSe_3：合成，晶体结构确定，拉曼光谱和离子电导率

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Na_3SbSe_3 was obtained by solid state reaction of anhydrous Na_2Se, antimony, and selenium in a ratio of 3:2:3. It is air and moisture sensitive and melts at 870 K. Yellow single crystals of Na _3SbSe_3 were used for single-crystal X-ray diffraction. It crystallizes in the cubic space group P213 (No. 198) with a = 9.0227(2) ?, V = 734.53(3) ?3, and Z = 4.Na)_3SbS_3 is isotypic with Na_3AsS_3. Trigonal SbSe3 pyramids therein act as mono-, bi-, and tridentate ligands to sodium. Sodium is located at three different sites, which are all coordinated by six selenium atoms, providing a strongly distorted octahedral environment. NaSe_6 octahedra of identical type share common vertices; in case of different sites also face sharing is observed. Na_3SbSe_3 shows temperature dependent Na+ conductivity above 380 K, which increases to 2.9>10-6 Ω-1 cm-1 at 590 K.
机译：Na_3SbSe_3通过无水Na_2Se，锑和硒的固相反应以3：2：3的比例获得。它对空气和湿气敏感，熔点为870K。Na_3SbSe_3的黄色单晶用于X射线单晶衍射。它在立方空间群P213（No. 198）中结晶，其a = 9.0227（2）α，V = 734.53（3）α3，Z = 4.Na）_3SbS_3与Na_3AsS_3同型。其中的三角形SbSe3金字塔充当钠的单齿，双齿和三齿配体。钠位于三个不同的位置，它们都由六个硒原子配位，从而提供了一个严重扭曲的八面体环境。相同类型的NaSe_6八面体共享共同的顶点;在不同站点的情况下，也观察到人脸共享。 Na_3SbSe_3在380 K以上显示出随温度变化的Na +电导率，在590 K时增加到2.9> 10-6Ω-1cm-1。