首页> 外文期刊>Zeitschrift fur Anorganische und Allgemeine Chemie >Preparation and crystal structure of sodium iron hydrogen phosphate, NaFe(HPO4)(H2PO4)(2) center dot H2O
【24h】

Preparation and crystal structure of sodium iron hydrogen phosphate, NaFe(HPO4)(H2PO4)(2) center dot H2O

机译：磷酸氢钠铁（NaFe（HPO4）（H2PO4）（2）中心点H2O的制备和晶体结构

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Single crystals of sodium iron hydrogen phosphate, NaFe(HPO4)(H2PO4)(2). H2O, were prepared hydrothermally by heating a mixture of Fe2O3, H3PO4 and Na2CO3 with a small amount of water. It crystallizes orthorhombic (Pbcn (N degrees 60), Z = 8, a = 872.91(7), b = 1249.54(8), c = 1894.4(1) pm). The crystal structure was solved by using 1121 unique reflections I > 2 sigma(I) and refined for a final conventional residual R = 0.039 (188 variables, 25 atoms including hydrogen in the asymmetric unit). The main feature of the crystal structure is a ReO3-like network formed by hydrogenphosphate-, dihydrogenphosphate-groups and FeO6 octahedra with channels along the [201], [010] and [<(2)over bar 01>] directions. Na+ and H2O molecules are occupying these channels. Effective Coordination Numbers (ECoN), Mean Fictive Ionic Radii (MEFIR) and the Madelung Part of Lattice Energy (MAPLE) are calculated for the title compound. [References: 12]
机译：磷酸氢铁钠铁的单晶NaFe（HPO4）（H2PO4）（2）。通过加热Fe2O3，H3PO4和Na2CO3的混合物与少量水以水热方式制备H2O。它结晶成斜方晶系（Pbcn（N度60），Z = 8，a = 872.91（7），b = 1249.54（8），c = 1894.4（1）pm）。通过使用1121个唯一反射I> 2 sigma（I）解析晶体结构，并精炼为最终的常规残留R = 0.039（188个变量，在不对称单元中包括25个原子）。晶体结构的主要特征是由磷酸氢根，磷酸二氢根和FeO6八面体形成的ReO3样网络，其通道沿[201]，[010]和[<（2）穿过条01>]方向。 Na +和H2O分子占据了这些通道。计算出标题化合物的有效配位数（ECoN），平均虚拟离子半径（MEFIR）和格架能量的马德隆部分（MAPLE）。 [参考：12]