首页> 外文期刊>Zeitschrift fur Anorganische und Allgemeine Chemie >SYNTHESIS AND STRUCTURE OF LI2TA2O3F6 [German]
【24h】

SYNTHESIS AND STRUCTURE OF LI2TA2O3F6 [German]

机译：Li2TA2O3F6的合成与结构[德语]

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Colourless crystals of Li2Ta2O3F6 are obtained by heating a mixture of LiTaF6 and LiTaO3 in a sealed nickel tube to 700 degrees C for 5 days, followed by slow cooling to room temperature. Li2Ta2O3F6 is also a product of controlled hydrolysis of LiTaF6. It crystallizes in the trigonal space group P3(1)21 with a = 558.11(3), c = 2096.10(4) pm, and Z = 3. The structure is built up by corner-sharing TaO3F3-octahedra forming anionic double layers parallel (001). The lithium cations are intercalated between these double layers having a square-pyramidal coordination by fluorine atoms. For the educt LiTaF6 a new high-temperature modification was found, which is reversibly formed at 150 degrees C. It crystallizes with a = 783.5 pm in the cubic NaSbF6 type. [References: 17]
机译：通过在密封的镍管中将LiTaF6和LiTaO3的混合物加热至700摄氏度5天，然后缓慢冷却至室温，可获得Li2Ta2O3F6的无色晶体。 Li2Ta2O3F6也是LiTaF6受控水解的产物。它在三边形空间群P3（1）21中结晶，a = 558.11（3），c = 2096.10（4）pm，Z =3。该结构由角共享的TaO3F3-八面体构成，形成平行的阴离子双层（001）。锂阳离子被氟原子插入具有方锥体配位的这些双层之间。对于离析物LiTaF6，发现了一种新的高温修饰，该修饰在150℃可逆地形成。在立方晶NaSbF6型中，其结晶度为a = 783.5 pm。 [参考：17]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号