首页> 外文期刊>Zeitschrift fur Naturforschung, B. A Journal of Chemical Sciences >High-pressure high-temperature decomposition of CeCoGa to the Laves phases CeCo0.58Ga1.42,CeCo0.72Ga1.28, and CeCo2
【24h】

High-pressure high-temperature decomposition of CeCoGa to the Laves phases CeCo0.58Ga1.42,CeCo0.72Ga1.28, and CeCo2

机译：CeCoGa的高压高温分解为Laves相CeCo0.58Ga1.42，CeCo0.72Ga1.28和CeCo2

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The monoclinic intermediate-valent gallide CeCoGa decomposes under high-pressure (HP) (9.5 GPa) high-temperature (HT) (1470 K) conditions into the Laves phases CeCo0.58 Ga-1.42 (MgCu2 type), CeCo0.72 Ga-1.28 (MgZn2 type; major product phase), and CeCo2 (MgCu2 type). The structures of the ternary Laves phases were refined from single crystal X-ray diffractometer data: Fd (3) over barm, a = 778.3(1) pm, wR2 = 0.0310, 63 F-2 values, five variables for CeCo (0.58(3)) Ga (1.42(3)) and P6(3)/mmc, a = 547.24(5), c = 858.76(7) pm, wR2 = 0.1009, 195 F-2 values, 13 variables for CeCo (0.72(1)) Ga (1.28(1)). Partial substitution of cobalt by gallium leads to a significant increase of the distances within the tetrahedral network: 253 pm Co-Co in CeCo2 as compared to 275 pm in CeCo0.58(3) Ga (1.42(3)) and 265-277 pm in CeCo (0.72(1)) Ga-1.28(1). The crystal chemical consequences are briefly discussed.
机译：单斜晶系中等价镓化物CeCoGa在高压（HP）（9.5 GPa）高温（HT）（1470 K）条件下分解成Laves相CeCo0.58 Ga-1.42（MgCu2型），CeCo0.72 Ga- 1.28（MgZn2型;主要产品相）和CeCo2（MgCu2型）。从单晶X射线衍射仪数据中精制了三元Laves相的结构：bard上的Fd（3），a = 778.3（1）pm，wR2 = 0.0310，63 F-2值，CeCo的五个变量（0.58（ 3））Ga（1.42（3））和P6（3）/ mmc，a = 547.24（5），c = 858.76（7）pm，wR2 = 0.1009，195 F-2值，CeCo的13个变量（0.72（ 1））Ga（1.28（1））。用镓部分取代钴会导致四面体网络内距离的显着增加：CeCo2中Co-Co的253 pm，而CeCo0.58（3）Ga（1.42（3））和265-277 pm的275 pm在CeCo（0.72（1））Ga-1.28（1）中。简要讨论了晶体化学后果。